Polyether Imide (PEI) Ultem 1010 is an amorphous, amber to transparent thermoplastics with a glass transition temperature (Tg) of 217 °C and performs in continuous use up to 170 °C. This inherently flame retardant plastic has UL94 V0 and 5VA ratings.
The PrimaCreator PEI Filament has unique properties because it does not come into contact with water during the production process and is directly packaged in a vacuum packaging. These properties make the PrimaCreator PEI Filament particularly suitable for usage in FDM and FFF 3D printers. The material has an excellent adhesion between layers which results in great improvement of the impact resistance, strength, durability and the printing process.
To make a successful PEI print there are a few things to keep in mind.
The printer must have the performance to meet the PEI filament and it should be printed with a nozzle temperature of 350-380°C. The heat bed should be set to 120-160°C and a heated chamber is important to have. It´s also very important to make sure that the printer is placed in a room where there´s hardly any draft and temperature fluctuations.
PEEK is best printed on a PEI sheet at a printing speed of 15-30 mm/s.
For further information, check the TDS
Diameter 1.75mm Tolerance ± 0.05 mm Heated build platform required Yes, 120-160° C Print Temperature 355 - 390° C Recommended Print Speed 15-30 mm/s Weight Filament 500 grams
Property Test method Value Density ISO 1183 1,27 g/cm3 Tensile Modulus ISO 527 3200 MPa Tensile Strength ISO 527 105 MPa Impact strength ISO 180 5 KJ/m2